Technical study on the production of blocks with composites of cement-wooden wastes from pallets of Pinus sp

Roger Alonso Moya Roque; Luis Diego Méndez-Mejías; Estephania Salazar-Zeledon; Maria José Esquivel-Fuentes

doi:10.7764/RDLC.18.1.5

Technical study on the production of blocks with composites of cement-wooden wastes from pallets of Pinus sp

Roger Alonso Moya Roque
, Luis Diego Méndez-Mejías
, Estephania Salazar-Zeledon
, Maria José Esquivel-Fuentes

Research output: Contribution to journal › Article › peer-review

1 Scopus citations

Abstract

A composite between particles obtained residual pallets of Pinus sp and cement was manufactured. Also, three methods were performance for wood particles: hot water washed, unwashed and unwashed with calcium carbonate (CaCO3). Different concrete-wood particle ratios were tested. Curing time was evaluated with ultrasonic pulse velocity (USV) and density of composites. Water absorption, module of rupture (MOR) in flexion, abrasion strength and resistance to decay by fungi attack were too determined. Results showed that using USV and density, curing occurs within 8 days. Moisture absorption ranges15 and 22% and decreases with decreasing of the amount of particles. MOR ranged from 0.40 a 1.23 MPa and the blocks with unwashed wooden particles and with CaCO₃ addition had the greatest significant differences. In abrasion strength, blocks with unwashed wooden particles reported the best results. Finally, it was concluded that mixture with proportion of 60:40 (concrete:wood) and CaCO₃ had the best performance and were not attacked by fungi decay.

Translated title of the contribution	Estudio técnico de la producción de bloques compuesto de cemento y tarimas recicladas de Pinus sp
Original language	English
Pages (from-to)	5-15
Number of pages	11
Journal	Revista de la construcción
Volume	18
Issue number	1
DOIs	https://doi.org/10.7764/RDLC.18.1.5 https://doi.org/10.7764/RDLC.18.1.5
State	Published - 1 Apr 2019

Keywords

Absorption
Concrete blocks
Construction material
Costa Rica
Wastes

Access to Document

10.7764/RDLC.18.1.5
10.7764/RDLC.18.1.5License: CC BY-NC-ND

Cite this

@article{d97e3e1ab3b74b00b426a775b0bc6083,

title = "Technical study on the production of blocks with composites of cement-wooden wastes from pallets of Pinus sp",

abstract = "Fue fabricado un compuesto de part{\'i}culas de Pinus spproveniente detarimas y 3 m{\'e}todos fueron practicados en las part{\'i}culas: lavado con agua caliente, sin lavar y sin lavar con adici{\'o}n de carbonato de calcio. Diferentes proporciones de cemento–maderas fueron probadas. El endurecimiento fue evaluado por la velocidad de pulso ultras{\'o}nico (VPU) y la densidad. As{\'i} mismo fue evaluado la absorci{\'o}n de agua, m{\'o}dulo de ruptura (MOR) en flexi{\'o}n, resistencia a la abrasi{\'o}n y resistencia al ataque de hongos de pudrici{\'o}n. Los resultados mostraron que utilizando VPU y densidad, el endurecimiento ocurre a los 8 d{\'i}as. La absorci{\'o}n de humedad fluct{\'u}a entre 15 y 22\% y disminuye con la disminuci{\'o}n de la cantidadde part{\'i}culas de madera. El MR vari{\'o} de 0,40 a 1,23 MPa y los adoquines con part{\'i}culas de madera sin lavar y agregado cal presentaron las mayores diferencias significativas. En la resistencia a la abrasi{\'o}n, los adoquines con part{\'i}culas de madera sin lavar reportan los mejores resultados. Finalmente se concluy{\'o} que la mezcla con proporciones de 60:40 (concreto: madera) y agregando calpresenta el mejor comportamiento y no son atacados por los hongos de pudrici{\'o}n.",

keywords = "Absorption, Concrete blocks, Construction material, Costa Rica, Wastes, Material de construcci{\'o}n,, residuos, absorci{\'o}n, adoquines, Costa Rica",

author = "\{Moya Roque\}, \{Roger Alonso\} and M{\'e}ndez-Mej{\'i}as, \{Luis Diego\} and Estephania Salazar-Zeledon and Esquivel-Fuentes, \{Maria Jos{\'e}\}",

note = "Publisher Copyright: {\textcopyright} 2019 Pontificia Universidad Catolica de Chile, Escuela de Construccion Civil.",

year = "2019",

month = apr,

day = "1",

doi = "10.7764/RDLC.18.1.5",

language = "Ingl{\'e}s",

volume = "18",

pages = "5--15",

journal = "Revista de la construcci{\'o}n",

number = "1",

}

TY - JOUR

T1 - Technical study on the production of blocks with composites of cement-wooden wastes from pallets of Pinus sp

AU - Moya Roque, Roger Alonso

AU - Méndez-Mejías, Luis Diego

AU - Salazar-Zeledon, Estephania

AU - Esquivel-Fuentes, Maria José

PY - 2019/4/1

Y1 - 2019/4/1

N2 - Fue fabricado un compuesto de partículas de Pinus spproveniente detarimas y 3 métodos fueron practicados en las partículas: lavado con agua caliente, sin lavar y sin lavar con adición de carbonato de calcio. Diferentes proporciones de cemento–maderas fueron probadas. El endurecimiento fue evaluado por la velocidad de pulso ultrasónico (VPU) y la densidad. Así mismo fue evaluado la absorción de agua, módulo de ruptura (MOR) en flexión, resistencia a la abrasión y resistencia al ataque de hongos de pudrición. Los resultados mostraron que utilizando VPU y densidad, el endurecimiento ocurre a los 8 días. La absorción de humedad fluctúa entre 15 y 22% y disminuye con la disminución de la cantidadde partículas de madera. El MR varió de 0,40 a 1,23 MPa y los adoquines con partículas de madera sin lavar y agregado cal presentaron las mayores diferencias significativas. En la resistencia a la abrasión, los adoquines con partículas de madera sin lavar reportan los mejores resultados. Finalmente se concluyó que la mezcla con proporciones de 60:40 (concreto: madera) y agregando calpresenta el mejor comportamiento y no son atacados por los hongos de pudrición.

AB - Fue fabricado un compuesto de partículas de Pinus spproveniente detarimas y 3 métodos fueron practicados en las partículas: lavado con agua caliente, sin lavar y sin lavar con adición de carbonato de calcio. Diferentes proporciones de cemento–maderas fueron probadas. El endurecimiento fue evaluado por la velocidad de pulso ultrasónico (VPU) y la densidad. Así mismo fue evaluado la absorción de agua, módulo de ruptura (MOR) en flexión, resistencia a la abrasión y resistencia al ataque de hongos de pudrición. Los resultados mostraron que utilizando VPU y densidad, el endurecimiento ocurre a los 8 días. La absorción de humedad fluctúa entre 15 y 22% y disminuye con la disminución de la cantidadde partículas de madera. El MR varió de 0,40 a 1,23 MPa y los adoquines con partículas de madera sin lavar y agregado cal presentaron las mayores diferencias significativas. En la resistencia a la abrasión, los adoquines con partículas de madera sin lavar reportan los mejores resultados. Finalmente se concluyó que la mezcla con proporciones de 60:40 (concreto: madera) y agregando calpresenta el mejor comportamiento y no son atacados por los hongos de pudrición.

KW - Absorption

KW - Concrete blocks

KW - Construction material

KW - Costa Rica

KW - Wastes

KW - Material de construcción,

KW - residuos

KW - absorción

KW - adoquines

KW - Costa Rica

UR - https://www.scopus.com/pages/publications/85066322248

U2 - 10.7764/RDLC.18.1.5

DO - 10.7764/RDLC.18.1.5

M3 - Artículo

AN - SCOPUS:85066322248

VL - 18

SP - 5

EP - 15

JO - Revista de la construcción

JF - Revista de la construcción

IS - 1

ER -

Technical study on the production of blocks with composites of cement-wooden wastes from pallets of Pinus sp

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this